Automotive Polyurethane Windshield Car Windscreen Glass PU Sealant

• CAS No.: 94766-07-1
• Formula: 94766-07-1
• Bonding Function: Car Adhesive
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: JB16
• Morphology: Solid-State
• Application: Automobile, Construction, Car Industry
• Material: Polyurethane
• Classification: Car
• Main Agent Composition: Polyurrethne
• Characteristic: Primer-Free
• Promoter Composition: Curing Agent
• Composition: Polyurethane
• Color: Black
• Transport Package: Box
• Specification: 310ml
• Trademark: Junbond
• Origin: China
• Production Capacity: 3000000
• Package Size: 30.00cm * 23.00cm * 24.00cm
• Package Gross Weight: 9.700kg
• Lead Time: 35 days (1 - 500000 Pieces) ; To be negotiated ( > 500000 Pieces)

Product Description

 

Product Description

Description:polyurethane sealant windshield sealant

 

PUJB16 is a one-part room temperature curing polyurethane with high peel strength,good elasticity, aging resistant, vibration exhaustion resistant, low temperature resistant and multi-coatings paintable and easy application properties.

It is one Component, Moisture Curing Polyurethane Based Multipurpose PU Adhesive  Sealant For Auto Windscreen, & direct glazing in Automotive Glass Replacement. Maxtech PUJB16 is  A Black Auto Glass Sealant (Primerless) Windscreen Replacement Polyurethane Sealant glue.

Features

 

Key Features:

No Sagging

Primerless

Excellent thixotropy, non-sag properties

Fast adhesion to substrates

Cold application

One-component formulation

No oil permeated

Paintable, abrasion able

Convenient to apply

Good aging resistance and weather resistance

High mechanical performance

High Modulus

High initial bond strength

Application

 

Areas of Application:

PU It is designed for maintenance and sealing for auto windows, it also is used for the direction for auto windshield glass, Windshield Bonding and Car Body Repair, Car window bonding . It is especially useful in bonding windshield glass into automotive frames
 

Tack free time min	30-90
Curing speed mm/24hrs	3-5
Solid content % ≥	95
Extrudability g/min ≥	80
Shore A hardness (±)	60
Density g/cm³ (±)	1.4
Tensile Strength Mpa ≥	4.2
Elongation at break % ≥	340
Tear Strength Mpa ≥	12
Shear strength N/mm ≥	4.5
Service Temperature	-40ºC ~80ºC