| Customization: | Available |
|---|---|
| Capacity: | 400ml |
| Color: | Custom |
|
Still deciding? Get samples of US$ 30/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| No. | Test Itema | Requirement of Criterion T/CECS 10158-2021 Table 1 |
Test results | Item Conclusion | Test Method | |
| 1 | Volatile organic compound (VOC) | ≤40g/kg | 11.0g/kg | Pass | T/CECS 10158-2021 6.3.1 GB/T 23985-2009 |
|
| 2 | Free formaldehyde | ≤0.1g/kg | Not Detected | Pass | GB 18583-2008 Appendix A | |
| 3 | Benzene | ≤0.1g/kg | Not Detected | Pass | T/CECS 10158-2021 6.3.3 GB/T 23990-2009 Method A |
|
| 4 | The sum of toluene, xylene and ethylbenzene | ≤5g/kg | Not Detected | Pass | T/CECS 10158-2021 6.3.3 GB/T 23990-2009 Method A |
|
| 5 | Appearance | Uniform and fine, no obvious bubbles and particles | Uniform and fine, no obvious bubbles and particles | Pass | T/CECS 10158-2021 6.4.1 | |
| 6 | Slump(vertical) | ≤3mm | 0mm | Pass | T/CECS 10158-2021 6.4.3 | |
| 7 | Drying time | Surface drying time | ≤1h | 45min | Pass | T/CECS 10158-2021 6.4.2 GB/T 1728-2020 7.3.1 Method A |
| Hard drying time |
≤5h | 3h30min | Pass | |||
| 8 | Resistance to abrasion | ≤40mg | 17mg | Pass | GB/T 1768-2006 | |
| 9 | Shore hardness | ≥50 | 65 | Pass | T/CECS 10158-2021 6.4.5 | |
| 10 | Flexibility(film thickness 1mm) | ≤3mm | 2mm | Pass | T/CECS 10158-2021 6.4.4 | |
| 11 | Resistance to water(168h) | No blistering, no flaking, no obviously color change | No blistering, no flaking, no obviously color change | Pass | T/CECS 10158-2021 6.4.8 | |
| 12 | Resistance to acid and alkali | Resistance to alkali(5% NaOH, 24h) | No blistering, no flaking, no obviously color change | No blistering, no flaking, no obviously color change | Pass | T/CECS 10158-2021 6.4.9 |
| Resistance to acid(5% H2SO4, 24h) | No blistering, no flaking, no obviously color change | No blistering, no flaking, no obviously color change | Pass | |||
| 13 | Pollution Resistance | Red wine | ≤2 rank | 1 rank | Pass | T/CECS 10158-2021 6.4.10 |
| Black tea | 1 rank | Pass | ||||
| Soy sauce | 1 rank | Pass | ||||
| Edible vinegar | 1 rank | Pass | ||||
| 14 | Yellowing resistance | <1 rank | 0 rank | Pass | T/CECS 10158-2021 6.4.11 | |
| 15 | Tensile strength | ≥12MPa | 14MPa | Pass | T/CECS 10158-2021 6.4.12 GB/T 528-2009 |
|
| 16 | Bond strength | Standard condition | ≥3MPa | 3.4MPa | Pass | T/CECS 10158-2021 6.4.13 GB/T 5210-2006 |
| Heat aging | ≥3MPa | 3.5MPa | Pass | |||
| Water immersion | ≥3MPa | 3.4MPa | Pass | |||
| 17 | Glossiness(60°) | Agreed | 78 | - | GB/T 9754-2007 | |
| Remark |
|
|||||
){kind=link}