No Ethylenediamine Floor Tile Grout Gold Tile Grout Ceramic Floor Tile Sealant for Grout

• Customization: Available
• Capacity: 400ml
• Color: Custom
• Model NO.: grout
• Drying Time: 2 Hours
• Material: Epoxy
• Usage: Home Improvement
• Appearance: Smooth Paste
• Surface Dry Time: 30-50mins
• Remove Redundance Time: 6-8 H
• Fully Dry Time: 12h(Over 10ºC) or 24h(Under 10ºC)
• Anti-Yellowing: 0.93 (168h/△e)
• Shelf Life: 12 Month
• Raw Material: Polyurea
• Specifications: 400ml
• Trademarks: OEM
• Transport Package: 24/50 PC in Box
• Specification: 47*28*24cm
• Trademark: Junbond
• Origin: China
• HS Code: 3506100010
• Production Capacity: 115 Tons/Day
• Package Size: 345.00cm * 1.00cm * 22.00cm
• Package Gross Weight: 1.000kg

Product Description

Yellowing resistance Marble tile Adhesive epoxy grout for tile waterproof bathroom grout

Ceramic Tile Sealer is a two component resin modified sealant which is made from two different resins fillers of great bonding strength and moisture resistance than cement. Epoxy tile grout has become popular due to its superior advantage, like strong bonding, high gloss decoration effect, strong anti-mildew effect, etc.

Aplication
1. All kinds of cabinets aperture, window, furniture, etc
2. All kinds of edges of Kitchen, toilet, also can be used to paste all kinds of hard materials
3. Bathtub, shower room, glass partition, implement, lavabo, mesa and basins of guesthouse
4. Hotel, family, such as the installation of sanitary ware, waterproof, plugging and decoration processing.
 

No.	Test Itema		Requirement of Criterion T/CECS 10158-2021 Table 1	Test results	Item Conclusion	Test Method
1	Volatile organic compound (VOC)		≤40g/kg	11.0g/kg	Pass	T/CECS 10158-2021 6.3.1 GB/T 23985-2009
2	Free formaldehyde		≤0.1g/kg	Not Detected	Pass	GB 18583-2008 Appendix A
3	Benzene		≤0.1g/kg	Not Detected	Pass	T/CECS 10158-2021 6.3.3 GB/T 23990-2009 Method A
4	The sum of toluene, xylene and ethylbenzene		≤5g/kg	Not Detected	Pass	T/CECS 10158-2021 6.3.3 GB/T 23990-2009 Method A
5	Appearance		Uniform and fine, no obvious bubbles and particles	Uniform and fine, no obvious bubbles and particles	Pass	T/CECS 10158-2021 6.4.1
6	Slump(vertical)		≤3mm	0mm	Pass	T/CECS 10158-2021 6.4.3
7	Drying time	Surface drying time	≤1h	45min	Pass	T/CECS 10158-2021 6.4.2 GB/T 1728-2020 7.3.1 Method A
		Hard drying time	≤5h	3h30min	Pass
8	Resistance to abrasion		≤40mg	17mg	Pass	GB/T 1768-2006
9	Shore hardness		≥50	65	Pass	T/CECS 10158-2021 6.4.5
10	Flexibility(film thickness 1mm)		≤3mm	2mm	Pass	T/CECS 10158-2021 6.4.4
11	Resistance to water(168h)		No blistering, no flaking, no obviously color change	No blistering, no flaking, no obviously color change	Pass	T/CECS 10158-2021 6.4.8
12	Resistance to acid and alkali	Resistance to alkali(5% NaOH, 24h)	No blistering, no flaking, no obviously color change	No blistering, no flaking, no obviously color change	Pass	T/CECS 10158-2021 6.4.9
		Resistance to acid(5% H2SO4, 24h)	No blistering, no flaking, no obviously color change	No blistering, no flaking, no obviously color change	Pass
13	Pollution Resistance	Red wine	≤2 rank	1 rank	Pass	T/CECS 10158-2021 6.4.10
		Black tea		1 rank	Pass
		Soy sauce		1 rank	Pass
		Edible vinegar		1 rank	Pass
14	Yellowing resistance		<1 rank	0 rank	Pass	T/CECS 10158-2021 6.4.11
15	Tensile strength		≥12MPa	14MPa	Pass	T/CECS 10158-2021 6.4.12 GB/T 528-2009
16	Bond strength	Standard condition	≥3MPa	3.4MPa	Pass	T/CECS 10158-2021 6.4.13 GB/T 5210-2006
		Heat aging	≥3MPa	3.5MPa	Pass
		Water immersion	≥3MPa	3.4MPa	Pass
17	Glossiness(60°)		Agreed	78	-	GB/T 9754-2007
Remark	Test location: GuanZhuang. Not Detected: Free formaldehyde<0.05g/kg; Benzene, toluene, xylene and ethylbenzene were all <0.05g/kg