Automotive Glass Auto Windshield Sealant

• CAS No.: 94766-07-1
• Formula: 94766-07-1
• Bonding Function: Car Adhesive
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Morphology: Solid-State
• Application: Automobile, Construction
• Material: Polyurethane
• Classification: Car
• Main Agent Composition: PU Car Glass
• Characteristic: High Strength Fast Bonding
• Promoter Composition: Curing Agent
• Composition: Polyurethane
• Color: Black
• Specification: 300ml
• Trademark: Junbond
• Origin: China
• Production Capacity: 3000000
• Package Size: 30.00cm * 23.00cm * 24.00cm
• Package Gross Weight: 15.000kg
• Lead Time: 15 days (1 - 500000 Pieces) ; To be negotiated ( > 500000 Pieces)

Product Description

 

Product Description

Description:polyurethane sealant windshield sealant

 

PUJB16 is a one-part room temperature curing polyurethane with high peel strength,

good elasticity, aging resistant, vibration exhaustion resistant, low temperature

resistant and multi-coatings paintable and easy application properties.

It is one Component, Moisture Curing Polyurethane Based Multipurpose PU Adhesive  Sealant For Auto Windscreen, & direct glazing in Automotive Glass Replacement. Maxtech PUJB16 is  A Black Auto Glass Sealant (Primerless) Windscreen Replacement Polyurethane Sealant glue.

 

Key Features

No Sagging

Primerless

Excellent thixotropy, non-sag properties

Fast adhesion to substrates

Cold application

One-component formulation

No oil permeated

Paintable, abrasion able

Convenient to apply

Good aging resistance and weather resistance

High mechanical performance

High Modulus

 High initial bond strength

 

Areas of Application

 

PU1731 It is designed for maintenance and sealing for auto windows, it also is used for the direction for auto windshield glass, Windshield Bonding and Car Body Repair, Car window bonding . It is especially useful in bonding windshield glass into automotive frames

Tack free time min	30-90
Curing speed mm/24hrs	3-5
Solid content % ≥	95
Extrudability g/min ≥	80
Shore A hardness (±)	60
Density g/cm³ (±)	1.4
Tensile Strength Mpa ≥	4.2
Elongation at break % ≥	340
Tear Strength Mpa ≥	12
Shear strength N/mm ≥	4.5
Service Temperature	-40ºC ~80ºC